Polymaker 2.85mm PolyMide PA6-CF Filament (500g, Black)

Polymaker PolyMide PA6-CF 2.875mm Overview

PolyMide PA6-CF from Polymaker is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly enhanced stiffness, strength, and heat resistance with outstanding layer adhesion. PolyMide PA6-CF is from the PolyMide family of Nylon/polyamide based filaments and features Polymaker's Warp-Free technology, which allows the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.

PolyMide PA6-CF is compatible with most of the 3D printers available on the market. Examples include the Ultimaker, Flashforge, Snapmaker, LulzBot, Raise3D, Flsun, Artillery, Anycubic, Creality, and more.

Please check out the below print settings and other properties, which are based on the use of a 0.4mm nozzle and the Simplify 3D v.4.0 printer.

Print Settings

Nozzle Temperature

536 to 572° F

Printing Speed

30 to 60mm/s

Bed Temperature

77 to 122° F

Bed Surface

Almost any surface with a thin coat of PVA glue or Magigoo PA

Cooling Fan

Off

Mechanical Properties

Young's Modulus

7453 ± 656 MPa

Tensile Strength

105.0 ± 5.0 MPa

Bending Strength

169.0 ± 4.7 MPa

Charpy Impact Strength

13.34 ± 0.52 kJ/m2

Thermal Properties

Heat Deflection Temperature

ISO 75 1.8 MPa: 384.8° F / ISO 75 0.45 MPa: 419° F

Melting Temperature

428° F

Other

Drying Settings

212° F for eight hours

Recommended Support Materials

PolyDissolve S1

Annealing

176° F for six hours

Sheet Resistance in Moisture State

(ASTM D991, GB/T 2439, ISO 1853) / 1 - 10 (108 /sq)