PolyMide PA6-CF from Polymaker is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly enhanced stiffness, strength, and heat resistance with outstanding layer adhesion. PolyMide PA6-CF is from the PolyMide family of Nylon/polyamide based filaments and features Polymaker s Warp-Free technology, which allows the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.
PolyMide PA6-CF is compatible with most of the 3D printers available on the market. Examples include the Ultimaker, Flashforge, Snapmaker, LulzBot, Raise3D, Flsun, Artillery, Anycubic, Creality, and more.
Please check out the below print settings and other properties, which are based on the use of a 0.4mm nozzle and the Simplify 3D v.4.0 printer.
Print Settings
Nozzle Temperature
536 to 572° F
Printing Speed
30 to 60mm/s
Bed Temperature
77 to 122° F
Bed Surface
Almost any surface with a thin coat of PVA glue or Magigoo PA
Cooling Fan
Off
Mechanical Properties
Young s Modulus
7453 ± 656 MPa
Tensile Strength
105.0 ± 5.0 MPa
Bending Strength
169.0 ± 4.7 MPa
Charpy Impact Strength
13.34 ± 0.52 kJ/m2
Thermal Properties
Heat Deflection Temperature
ISO 75 1.8 MPa: 384.8° F / ISO 75 0.45 MPa: 419° F
Melting Temperature
428° F
Other
Drying Settings
212° F for eight hours
Recommended Support Materials
PolyDissolve S1
Annealing
176° F for six hours
Sheet Resistance in Moisture State
(ASTM D991, GB/T 2439, ISO 1853) / 1 - 10 (108 Ω /sq)